Alkali metal electrochemical cell activated with a nonaqueous electrolyte having a sulfite additive

ABSTRACT

An alkali metal, solid cathode, nonaqueous electrochemical cell capable of delivering high current pulses, rapidly recovering its open circuit voltage and having high current capacity, is described. The stated benefits are realized by the addition of at least one organic sulfite additive to an electrolyte comprising an alkali metal salt dissolved in a mixture of a low viscosity solvent and a high permittivity solvent. A preferred solvent mixture includes propylene carbonate, dimethoxyethane and a sulfite additive having at least one unsaturated hydrocarbon containing a C(sp 2  or sp 3 )—C(sp 3 ) bond unit having the C(sp 3 ) carbon directly connected to the —OSO 2 — functional group.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority based on provisional application Serial No. 60/117,105, filed Jan. 25, 1999.

BACKGROUND OF INVENTION

1. Field of the Invention

The present invention generally relates to an alkali metal electrochemical cell, and more particularly, to an alkali metal cell suitable for current pulse discharge applications with reduced or no appreciable voltage delay.

2. Prior Art

The voltage response of a cell which does not exhibit voltage delay during the application of a short duration pulse or pulse train has distinct features. First, the cell potential decreases throughout the application of the pulse until it reaches a minimum at the end of the pulse, and second, the minimum potential of the first pulse in a series of pulses is higher than the minimum potential of the last pulse. FIG. 1 is a graph showing an illustrative discharge curve 10 as a typical or “ideal” response of a cell during the application of a series of pulses as a pulse train that does not exhibit voltage delay.

On the other hand, the voltage response of a cell which exhibits voltage delay during the application of a short duration pulse or during a pulse train can take one or both of two forms. One form is that the leading edge potential of the first pulse is lower than the end edge potential of the first pulse. In other words, the voltage of the cell at the instant the first pulse is applied is lower than the voltage of the cell immediately before the first pulse is removed. The second form of voltage delay is that the minimum potential of the first pulse is lower than the minimum potential of the last pulse when a series of pulses have been applied. FIG. 2 is a graph showing an illustrative discharge curve 12 as the voltage response of a cell that exhibits both forms of voltage delay.

The initial drop in cell potential during the application of a short duration pulse reflects the resistance of the cell, i.e., the resistance due to the cathode, the cathode-electrolyte interphase, the anode, and the anode-electrolyte interphase. In the absence of voltage delay, the resistance due to passivated films on the anode and/or cathode is negligible. However, the formation of a surface film is unavoidable for alkali metal, and in particular, lithium metal anodes, and for lithium intercalated carbon anodes, due to their relatively low potential and high reactivity towards organic electrolytes. Thus, the ideal anode surface film should be electrically insulating and ionically conducting. While most alkali metal, and in particular, lithium electrochemical systems meet the first requirement, the second requirement is difficult to achieve. In the event of voltage delay, the resistance of these films is not negligible, and as a result, impedance builds up inside the cell due to this surface layer formation which often results in reduced discharge voltage and reduced cell capacity. In other words, the drop in potential between the background voltage and the lowest voltage under pulse discharge conditions, excluding voltage delay, is an indication of the conductivity of the cell, i.e., the conductivity of the cathode, anode, electrolyte, and surface films, while the gradual decrease in cell potential during the application of the pulse train is due to the polarization of the electrodes and electrolyte.

Thus, the existence of voltage delay is an undesirable characteristic of alkali metal/mixed metal oxide cells subjected to current pulse discharge conditions in terms of its influence on devices such as medical devices including implantable pacemakers and cardiac defibrillators. Voltage delay is undesirable because it limits the effectiveness and even the proper functioning of both the cell and the associated electrically powered device under current pulse discharge conditions.

The present invention is directed to the provision of sulfite additives in the electrolyte of an alkali metal electrochemical cell to beneficially modify the anode surface film. The sulfite additives preferably include at least one unsaturated hydrocarbon containing a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon directly connected to the —OSO₂— functional group, and are provided as a co-solvent with commonly used organic aprotic solvents. When used as a co-solvent in an activating electrolyte, the sulfite additives interact with the alkali metal anode to form an ionically conductive surface protective layer thereon. The conductive surface layer improves the discharge performance of the alkali metal electrochemical cell and minimizes or even eliminates voltage delay in the high current pulse discharge of such cells.

SUMMARY OF THE INVENTION

The object of the present invention is to improve the pulse discharge performance of an alkali metal electrochemical cell, and more particularly a primary lithium electrochemical cell, by the provision of at least one of a family of sulfite additives as a co-solvent in the cell's activating nonaqueous electrolyte solution. Due to the high reduction potential of the sulfite group vs. lithium, the sulfite additives can compete effectively with the other electrolyte co-solvents or the solute to react with the lithium anode. Lithium sulfite or the lithium salt of sulfite reduction products are believed to be the major reaction products. These lithium salts are believed to deposit on the anode surface to form an ionically conductive protective film thereon. As a consequence, the chemical composition and perhaps the morphology of the anode surface protective layer is changed, and this proves beneficial to the discharge characteristics of the cell. The thusly fabricated cell exhibits reduced or no appreciable voltage delay under current pulse discharge usage, which is an unexpected result.

These and other objects of the present invention will become increasingly more apparent to those skilled in the art by reference to the following description and to the appended drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing an illustrative pulse discharge curve 10 of an exemplary electrochemical cell that does not exhibit voltage delay.

FIG. 2 is a graph showing an illustrative pulse discharge curve 12 of an exemplary electrochemical cell that exhibits voltage delay.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

As used herein, the term “pulse” means a burst of electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse. A pulse train consists of at least two pulses of electrical current delivered in relatively short succession with or without open circuit rest between the pulses. Voltage delay is calculated as the pulse end potential minus the pulse minimum potential.

The electrochemical cell of the present invention includes an anode selected from Group IA, IIA or IIIB of the Periodic Table of Elements, including lithium, sodium, potassium, etc., and their alloys and intermetallic compounds including, for example Li—Si, Li—B and Li—Si—B alloys and intermetallic compounds. The preferred anode comprises lithium, and the more preferred anode comprises a lithium alloy, the preferred lithium alloy being a lithium-aluminum alloy. The greater the amount of aluminum present by weight in the alloy, however, the lower the energy density of the cell.

The form of the anode may vary, but preferably the anode is a thin metal sheet or foil of the anode metal, pressed or rolled on a metallic anode current collector, i.e., preferably comprising nickel, to form an anode component. In the exemplary cell of the present invention, the anode component has an extended tab or lead of the same material as the anode current collector, i.e., preferably nickel, integrally formed therewith such as by welding and contacted by a weld to a cell case of conductive metal in a case-negative electrical configuration. Alternatively, the anode may be formed in some other geometry, such as a bobbin shape, cylinder or pellet to allow an alternate low surface cell design.

The cathode is preferably of a solid material and the electrochemical reaction at the cathode involves conversion of ions which migrate from the anode to the cathode in atomic or molecular forms. The solid cathode material may comprise a metal, a metal oxide, a mixed metal oxide, a metal sulfide or a carbonaceous compound, and combinations thereof. The metal oxide, the mixed metal oxide and the metal sulfide can be formed by the chemical addition, reaction, or otherwise intimate contact of various metal oxides, metal sulfides and/or metal elements, preferably during thermal treatment, sol-gel formation, chemical vapor deposition or hydrothermal synthesis in mixed states. The active materials thereby produced contain metals, oxides and sulfides of Groups IB, IIB, IIIB, IVB, VB, VIB, VIIB and VIII, which includes the noble metals and/or other oxide and sulfide compounds.

One preferred mixed metal oxide has the general formula SM_(x)V₂O_(y) wherein SM is a metal selected from Groups IB to VIIB and VIII of the Periodic Table of Elements, wherein x is about 0.30 to 2.0 and y is about 4.5 to 6.0 in the general formula. By way of illustration, and in no way intended to be limiting, one exemplary cathode active material comprises silver vanadium oxide (SVO) having the general formula Ag_(x)V₂O_(y) in any one of its many phases, i.e., β-phase silver vanadium oxide having in the general formula x=0.35 and y=5.8, γ-phase silver vanadium oxide having in the general formula x=0.80 and y=5.40 and ε-phase silver vanadium oxide having in the general formula x=1.0 and y=5.5, and combination and mixtures of phases thereof. For a more detailed description of such a cathode active material reference is made to U.S. Pat. No. 4,310,609 to Liang et al., which is assigned to the assignee of the present invention and incorporated herein by reference.

Another preferred composite cathode active material includes V₂O_(z) wherein z≦5 combined with Ag₂O with the silver in either the silver(II), silver(I) or silver(0) oxidation state and CuO with the copper in either the copper(II), copper(I) or copper(0) oxidation state to provide the mixed metal oxide having the general formula Cu_(x)Ag_(y)V₂O_(z), (CSVO). Thus, this composite cathode active material may be described as a metal oxide-metal oxide-metal oxide, a metal-metal oxide-metal oxide, or a metal-metal-metal oxide and the range of material compositions found for Cu_(x)Ag_(y)V₂O_(z) is preferably about 0.01≦x≦1.0, about 0.01≦y≦1.0 and about 5.01≦z≦6.5. Typical forms of CSVO are Cu_(0.16)Ag_(0.67)V₂O_(z) with z being about 5.5 and Cu_(0.5)Ag_(0.5)V₂O_(z) with z being about 5.75. The oxygen content is designated by z since the exact stoichiometric proportion of oxygen in CSVO can vary depending on whether the cathode material is prepared in an oxidizing atmosphere such as air or oxygen, or in an inert atmosphere such as argon, nitrogen and helium. For a more detailed description of this cathode active material reference is made to U.S. Pat. No. 5,472,810 to Takeuchi et al. and U.S. Pat. No. 5,516,340 to Takeuchi et al., both of which are assigned to the assignee of the present invention and incorporated herein by reference.

Additional cathode active materials include manganese dioxide, lithium cobalt oxide, lithium nickel oxide, copper vanadium oxide, vanadium oxide, titanium disulfide, copper oxide, copper sulfide, iron sulfide, iron disulfide, and fluorinated carbon, and mixtures thereof. Preferably, the cathode comprises from about 80 to about 99 weight percent of the cathode active material.

Cathode active materials prepared as described above are preferably mixed with a binder material such as a powdered fluoro-polymer, more preferably powdered polytetrafluoroethylene or powdered polyvinylidene fluoride present at about 1 to about 5 weight percent of the cathode mixture. Further, up to about 10 weight percent of a conductive diluent is preferably added to the cathode mixture to improve conductivity. Suitable materials for this purpose include acetylene black, carbon black and/or graphite or a metallic powder such as powdered nickel, aluminum, titanium and stainless steel. The preferred cathode active mixture thus includes a powdered fluoro-polymer binder present at about 3 weight percent, a conductive diluent present at about 3 weight percent and about 94 weight percent of the cathode active material. The cathode active mixture may be in the form of one or more plates operatively associated with at least one or more plates of anode material, or in the form of a strip wound with a corresponding strip of anode material in a structure similar to a “jellyroll”.

In order to prevent internal short circuit conditions, the cathode is separated from the Group IA, IIA or IIIB anode material by a suitable separator material. The separator is of electrically insulative material, and the separator material also is chemically unreactive with the anode and cathode active materials and both chemically unreactive with and insoluble in the electrolyte. In addition, the separator material has a degree of porosity sufficient to allow flow therethrough of the electrolyte during the electrochemical reaction of the cell. Illustrative separator materials include woven and non-woven fabrics of polyolefinic fibers or fluoropolymeric fibers including polyvinylidene fluoride, polyethylenetetrafluoroethylene, and polyethylenechlorotrifluoroethylene laminated or superposed with a polyolefinic or a fluoropolymeric microporous film. Suitable microporous films include a polytetrafluoroethylene membrane commercially available under the designation ZITEX (Chemplast Inc.), polypropylene membrane commercially available under the designation CELGARD (Celanese Plastic Company, Inc.) and a membrane commercially available under the designation DEXIGLAS (C. H. Dexter, Div., Dexter Corp.). The separator may also be composed of non-woven glass, glass fiber materials and ceramic materials.

The form of the separator typically is a sheet which is placed between the anode and cathode electrodes and in a manner preventing physical contact therebetween. Such is the case when the anode is folded in a serpentine-like structure with a plurality of cathode plates disposed intermediate the anode folds and received in a cell casing or when the electrode combination is rolled or otherwise formed into a cylindrical “jellyroll” configuration.

The electrochemical cell of the present invention further includes a nonaqueous, ionically conductive electrolyte operatively associated with the anode and the cathode electrodes. The electrolyte serves as a medium for migration of ions between the anode and the cathode during the electrochemical reactions of the cell and nonaqueous solvents suitable for the present invention are chosen so as to exhibit those physical properties necessary for ionic transport (low viscosity, low surface tension and wettability). Suitable nonaqueous solvents are comprised of an inorganic salt dissolved in a nonaqueous solvent and more preferably an alkali metal salt dissolved in a mixture of aprotic organic solvents comprising a low viscosity solvent including organic esters, ethers and dialkyl carbonates, and mixtures thereof, and a high permittivity solvent including cyclic carbonates, cyclic esters and cyclic amides, and mixtures thereof. Low viscosity solvents include tetrahydrofuran (THF), methyl acetate (MA), diglyme, triglyme, tetraglyme, 1,2-dimethoxyethane (DME), dimethyl carbonate (DMC), diisopropylether, 1,2-diethoxyethane, 1-ethoxy,2-methoxyethane, diethyl carbonate (DEC), dipropyl carbonate (DPC), ethyl methyl carbonate (EMC), methyl propyl carbonate (MPC) and ethyl propyl carbonate (EPC), and mixtures thereof. High permittivity solvents include propylene carbonate (PC), ethylene carbonate (EC), butylene carbonate (BC), acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, γ-valerolactone, γ-butyrolactone (GBL) and N-methyl-pyrrolidinone (NMP), and mixtures thereof.

The preferred electrolyte comprises an inorganic alkali metal salt, and in the case of an anode comprising lithium, the alkali metal salt of the electrolyte is a lithium based salt. Known lithium salts that are useful as a vehicle for transport of alkali metal ions from the anode to the cathode include LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiO₂, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄ and LiCF₃SO₃, and mixtures thereof. Suitable salt concentrations typically range between about 0.8 to 1.5 molar, and a preferred electrolyte for a lithium/transition metal oxide electrochemical cell includes LiAsF₆ or LiPF₆ dissolved in a 50:50 mixture, by volume, of PC and DME.

A distinguishing characteristic of a primary lithium metal cell, in comparison to that of a secondary lithium ion cell, is that the lithium anode material is consumed during discharge. In other words, the surface of the anode is shrinking or fading away from the electrode/electrolyte interphase during discharge. This is especially the case during high current pulse discharge when the anode surface passivation film breaks up to expose a fresh lithium surface. At this stage, a new passivation film forms and its chemical composition and surface morphology depends on the competition reactions of the existing components in the electrolyte, which, in turn, depends on the cell depth of discharge.

In a lithium/silver vanadium oxide cell, there are two characteristic voltage plateaus in the discharge profile. The first one occurs at about 3.2V and the second plateau occurs at about 2.6V. At the 3.2V discharge plateau, Li/SVO cells are known to be relatively stable and exhibit consistent long term pulse discharge behavior. This indicates that the lithium anode is effectively passivated by the electrolyte. However, when the cell is discharged to the 2.6V plateau, voltage delay is present in long term pulse discharge tests.

It has been determined that voltage delay in an alkali metal/transition metal oxide cell is caused by the growth of anode surface impedance. The chemical composition and the passivation ability of the anode surface layer have changed in the time that the Li/SVO cell has discharged from the 3.2V plateau to the 2.6V plateau. Consequently, the anode surface impedance increases over time and results in voltage delay during high current pulse discharge in long term tests.

In the absence of a sulfite additive to the electrolyte according to the present invention, the anode surface passivation film, which reforms on the newly exposed, fresh lithium surface during discharge, becomes more resistive ionically, or does not effectively passivate the anode electrically, and therefore, additional amounts of electrolyte decomposition occur on the anode surface. In turn, the impedance of the anode passivation layer increases over long term discharge tests, which results in unacceptable voltage delay and decreased pulse minimum potentials over those experienced without the undesirable anode surface passivation film. This is the reason for voltage delay during high current pulse discharge, especially in long term tests when the cell has been depleted of 40% to 70% of its capacity.

According to the present invention, the undesirable or “bad” passivation film formed on the lithium anode at the 2.6V depth of discharge in a Li/SVO cell is prevented by the presence of an electrically insulating and ionically conductive or “good” passivation layer formed on the anode surface. This passivation layer does not break up, or does not break up easily, during high current pulse discharge. If the passivation film does break up, it is readily reformed before an undesirable passivation layer replaces it. Thus, it is believed that exposure of fresh lithium is prevented or minimized during discharge.

An electrically insulating and ionically conducting or “good” passivation layer is formed on the lithium anode in accordance with the present invention by the provision of at least one sulfite additive as a co-solvent in the electrolyte solution of the previously described alkali metal electrochemical cell. The sulfite additive preferably has the general formula R¹OS(═O)(OR²), wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms.

The greatest effect is found when diallyl sulfite, methyl benzyl sulfite, ethyl benzyl sulfite, propyl benzyl sulfite, butyl benzyl sulfite, pentyl benzyl sulfite, methyl allyl sulfite, ethyl allyl sulfite, propyl allyl sulfite, butyl allyl sulfite, pentyl allyl sulfite, mono-methyl sulfite, mono-ethyl sulfite, mono-butyl sulfite, mono-propyl sulfite, mono-pentyl sulfite, mono-allyl sulfite, mono-benzyl sulfite and dibenzyl sulfite, and mixtures thereof are used as additives in the electrolyte.

The above described compounds are only intended to be exemplary of those that are useful with the present invention, and are not to be construed as limiting. Those skilled in the art will readily recognize sulfite compounds which come under the purview of the general formula set forth above and which will be useful as additives for the electrolyte to reduce voltage delay according to the present invention.

While not intending to be bound by any particular mechanism, it is believed that due to the presence of the sulfite additive comprising at least one unsaturated hydrocarbon containing a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon directly connected to the —OSO₂— functional group, the bond between oxygen and at least one of the group R¹ and R² is readily severed and the sulfite intermediate is able to compete effectively with the other electrolyte solvents or solutes to react with lithium and form a sulfite salt, i.e., lithium sulfite, or the lithium salt of a sulfite reduction product on the surface of the anode. The resulting salt is more conductive than lithium oxide which may form on the anode in the absence of the organic sulfite additive. In fact, it is believed that the lithium sulfite or the lithium salt of a sulfite reduction product on the surface of the anode provides for the existence of charge delocalization due to resonance equilibration at the anode surface. This equilibration allows lithium ions to travel easily from one molecule to the other via a lithium ion exchange mechanism. As a result, beneficial ionic conductance is realized. Accordingly, it is believed that the present organic sulfite compounds compete more effectively with the other solvents in the electrolyte to form an tonically more conductive and electrically more insulative film than is provided by alkyl sulfites and cyclic sulfites such as ethylene sulfite and propylene sulfite, for example.

During discharge, the lithium metal electrode is shrinking while the surface film moves continuously toward the lithium metal surface by following the lithium ion exchange mechanism. This process prevents the break up of the surface film and avoids the exposure of fresh lithium metal to the electrolyte. As a result, voltage delay in a lithium anode/transition metal oxide cell is minimized and even eliminated using electrolytes containing sulfite additives according to the present invention. As a consequence, the chemical composition and perhaps the morphology of the anode surface protective layer is believed to be changed with concomitant benefits to the cell's discharge characteristics.

In the present invention, the anode is lithium metal and the cathode is preferably the transition mixed metal oxide AgV₂O_(5.5) (SVO). The preferred electrolyte is 1.0M to 1.2M LiAsF₆ dissolved in an aprotic solvent mixture comprising at least one of the above listed low viscosity solvents and at least one of the above listed high permittivity solvents. The preferred aprotic solvent mixture comprises a 50/50, by volume, mixture of propylene carbonate and dimethoxyethane. The concentration of the above discussed sulfite additives according to the present invention should preferably be in the range of between about 0.001M to about 0.20M. The positive effects of these additives in reducing voltage delay in a pulse discharging alkali metal cell have been achieved both at room temperature as well as at temperatures up to about 37° C. This makes the novel electrolyte solution of the present invention particularly useful for activating an alkali metal/transition metal oxide cell incorporated into an implantable medical device such as a cardiac defibrillator to minimize or even eliminate voltage delay under high current pulse discharge conditions.

As is well known by those skilled in the art, an implantable cardiac defibrillator is a device that requires a power source for a generally medium rate, constant resistance load component provided by circuits performing such functions as, for example, the heart sensing and pacing functions. From time to time, the cardiac defibrillator may require a generally high rate, pulse discharge load component that occurs, for example, during charging of a capacitor in the defibrillator for the purpose of delivering an electrical shock to the heart to treat tachyarrhythmias, the irregular, rapid heartbeats that can be fatal if left uncorrected. Reduction and even elimination of voltage delay during a current pulse application is important for proper device operation and extended device life.

The assembly of the cell described herein is preferably in the form of a wound element cell. That is, the fabricated cathode, anode and separator are wound together in a “jellyroll” type configuration or “wound element cell stack” such that the anode is on the outside of the roll to make electrical contact with the cell case in a case-negative configuration. Using suitable top and bottom insulators, the wound cell stack is inserted into a metallic case of a suitable size dimension. The metallic case may comprise materials such as stainless steel, mild steel, nickel-plated mild steel, titanium, tantalum or aluminum, but not limited thereto, so long as the metallic material is compatible for use with components of the cell.

The cell header comprises a metallic disc-shaped body with a first hole to accommodate a glass-to-metal seal/terminal pin feedthrough and a second hole for electrolyte filling. The glass used is of a corrosion resistant type having up to about 50% by weight silicon such as CABAL 12, TA 23 or FUSITE 425 or FUSITE 435. The positive terminal pin feedthrough preferably comprises titanium although molybdenum, aluminum, nickel alloy, or stainless steel can also be used. The cell header comprises elements having compatibility with the other components of the electrochemical cell and is resistant to corrosion. The cathode lead is welded to the positive terminal pin in the glass-to-metal seal and the header is welded to the case containing the electrode stack. The cell is thereafter filled with the electrolyte solution comprising at least one of the sulfite additives described hereinabove and hermetically sealed such as by close-welding a stainless steel ball over the fill hole, but not limited thereto.

The above assembly describes a case-negative cell, which is the preferred construction of the exemplary cell of the present invention. As is well known to those skilled in the art, the exemplary electrochemical system of the present invention can also be constructed in a case-positive configuration.

It is appreciated that various modifications to the inventive concepts described herein may be apparent to those of ordinary skill in the art without departing from the spirit and scope of the present invention as defined by the appended claims. 

What is claimed is:
 1. An electrochemical cell, which comprises: a) an anode comprising an alkali metal; b) a cathode comprising a cathode active material; and c) a nonaqueous electrolyte activating the anode and the cathode, the nonaqueous electrolyte comprising: i) an additive of the general formula R¹OS(═O)(OR²) having at least one unsaturated hydrocarbon containing a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon directly connected to the —OSO₂— functional group, wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms; and ii) an alkali metal salt dissolved therein.
 2. The electrochemical cell of claim 1 wherein the additive is selected from the group consisting of diallyl sulfite, methyl benzyl sulfite, ethyl benzyl sulfite, propyl benzyl sulfite, butyl benzyl sulfite, pentyl benzyl sulfite, methyl allyl sulfite, ethyl allyl sulfite, propyl allyl sulfite, butyl allyl sulfite, pentyl allyl sulfite, mono-methyl sulfite, mono-ethyl sulfite, mono-butyl sulfite, mono-propyl sulfite, mono-pentyl sulfite, mono-allyl sulfite, mono-benzyl sulfite, dibenzyl sulfite, and mixtures thereof.
 3. The electrochemical cell of claim 1 wherein the additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 4. The electrochemical cell of claim 1 wherein the cell is dischargeable to deliver at least one current pulse of an electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse such that the pulse one end potential minus the pulse one minimum potential is less than about 200 mV.
 5. The electrochemical cell of claim 4 wherein there are at least two pulses delivered in succession with or without an open circuit period between the pulses.
 6. The electrochemical cell of claim 4 wherein the current pulses are of about 23.2 mA/cm².
 7. The electrochemical cell of claim 1 wherein the nonaqueous electrolyte comprises a first solvent selected from the group consisting of an ester, an ether, a dialkyl carbonate, and mixtures thereof, and a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester, a cyclic amide, and mixtures thereof.
 8. The electrochemical cell of claim 7 wherein the first solvent is selected from the group consisting of tetrahydrofuran, methyl acetate, diglyme, triglyme, tetraglyme, 1,2-dimethoxyethane, diisopropylether, 1,2-diethoxyethane, 1-ethoxy,2-methoxyethane, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethyl methyl carbonate, methyl propyl carbonate, ethyl propyl carbonate, and mixtures thereof.
 9. The electrochemical cell of claim 7 wherein the second solvent is selected from the group consisting of propylene carbonate, ethylene carbonate, butylene carbonate, acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, γ-valerolactone, γ-butyrolactone, N-methyl-pyrrolidinone, and mixtures thereof.
 10. The electrochemical cell of claim 1 wherein the alkali metal salt is selected from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiO₂, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄, LiCF₃SO₃, and mixtures thereof.
 11. The electrochemical cell of claim 1 wherein the solid cathode is selected from the group consisting of silver vanadium oxide, copper silver vanadium oxide, vanadium oxide, copper vanadium oxide, and mixtures thereof.
 12. The electrochemical cell of claim 1 wherein the anode is comprised of lithium or a lithium-aluminum alloy.
 13. The electrochemical cell of claim 1 wherein the cathode comprises from about 80 to about 99 weight percent of the cathode active material.
 14. The electrochemical cell of claim 1 wherein the cathode further comprises a binder material and a conductive additive.
 15. The electrochemical cell of claim 14 wherein the binder material is a fluoro-resin powder.
 16. The electrochemical cell of claim 14 wherein the conductive additive is selected from the group consisting of carbon, graphite powder, acetylene black, titanium powder, aluminum powder, nickel powder, stainless steel powder, and mixtures thereof.
 17. The electrochemical cell of claim 1 wherein the cathode comprises from about 0 to 3 weight percent carbon, about 1 to 5 weight percent of a powder fluoro-resin and about 94 weight percent of the cathode active material.
 18. The electrochemical cell of claim 1 wherein an implantable medical device is powered with the electrochemical cell.
 19. An electrochemical cell, which comprises: a) an anode comprising an alkali metal; b) a cathode including a mixed metal oxide comprised of vanadium oxide and a second metal “SM” selected from the group consisting of Groups IB, IIB, IIIB, IVB, VIB, VIIB and VIII of the Periodic Table of the Elements, the mixed metal oxide having the general formula SM_(x)V₂O_(y) wherein 0.30≦x≦2.0 and 4.5≦y≦6.0; c) a nonaqueous electrolyte activating the anode and the cathode, the nonaqueous electrolyte comprising: i) a first solvent selected from the group consisting of an ester, an ether, a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester, a cyclic amide, and mixtures thereof; iii) an additive of the general formula R¹OS(═O)(OR²) having at least one unsaturated hydrocarbon containing a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon directly connected to the —OSO₂— functional group, wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms; and iv) an alkali metal salt dissolved therein; and d) wherein the cell is dischargeable to deliver at least one current pulse of an electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse such that the pulse one end potential minus the pulse one minimum potential is less than about 200 mV.
 20. The electrochemical cell of claim 19 wherein the additive is selected from the group consisting of diallyl sulfite, methyl benzyl sulfite, ethyl benzyl sulfite, propyl benzyl sulfite, butyl benzyl sulfite, pentyl benzyl sulfite, methyl allyl sulfite, ethyl allyl sulfite, propyl allyl sulfite, butyl allyl sulfite, pentyl allyl sulfite, mono-methyl sulfite, mono-ethyl sulfite, mono-butyl sulfite, mono-propyl sulfite, mono-pentyl sulfite, mono-allyl sulfite, mono-benzyl sulfite, dibenzyl sulfite, and mixtures thereof.
 21. The electrochemical cell of claim 19 wherein the additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 22. An electrochemical cell, which comprises: a) an anode comprising an alkali metal; b) a cathode including a mixed metal oxide comprised of vanadium oxide and a mixture of copper and a second metal “SM” selected from the group consisting of groups IB, IIB, IIIB, IVB, VIB, VIIB, and VIII of the Periodic Table of the Elements, the mixed metal oxide having the general formula Cu_(x)SM_(y)V₂O_(z) wherein 0.01≦x≦1.0, 0.01≦y≦1.0 and 5.01≦z≦6.5; c) a nonaqueous electrolyte activating the anode and the cathode, the nonaqueous electrolyte comprising: i) a first solvent selected from the group consisting of an ester, an ether, a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester, a cyclic amide, and mixtures thereof; iii) an additive of the general formula R¹OS(═O)(OR²) having at least one unsaturated hydrocarbon directly connected to a C(sp² or sp³)—C (sp³) bond unit having the C(sp³) carbon connected to the —OSO₂— functional group, wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms; and iv) an alkali metal salt dissolved therein; and d) wherein the cell is dischargeable to deliver at least one current pulse of an electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse such that the pulse one end potential minus the pulse one minimum potential is less than about 200 mV.
 23. The electrochemical cell of claim 22 wherein the additive is selected from the group consisting of diallyl sulfite, methyl benzyl sulfite, ethyl benzyl sulfite, propyl benzyl sulfite, butyl benzyl sulfite, pentyl benzyl sulfite, methyl allyl sulfite, ethyl allyl sulfite, propyl allyl sulfite, butyl allyl sulfite, pentyl allyl sulfite, mono-methyl sulfite, mono-ethyl sulfite, mono-butyl sulfite, mono-propyl sulfite, mono-pentyl sulfite, mono-allyl sulfite, mono-benzyl sulfite, dibenzyl sulfite, and mixtures thereof.
 24. A method for reducing voltage delay in an electrochemical cell activated with a nonaqueous electrolyte, comprising the steps of: a) providing an anode comprising an alkali metal; b) providing a cathode comprising a cathode active material; c) activating the electrochemical cell with the nonaqueous electrolyte operatively associated with the anode and the cathode, the nonaqueous electrolyte comprising: i) an additive of the general formula R¹OS(═O)(OR²) having at least one unsaturated hydrocarbon containing a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon directly connected to the —OSO₂— functional group, wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms; and ii) an alkali metal salt dissolved therein; and d) discharging the cell.
 25. The method of claim 24 including selecting the additive from the group consisting of diallyl sulfite, methyl benzyl sulfite, ethyl benzyl sulfite, propyl benzyl sulfite, butyl benzyl sulfite, pentyl benzyl sulfite, methyl allyl sulfite, ethyl allyl sulfite, propyl allyl sulfite, butyl allyl sulfite, pentyl allyl sulfite, mono-methyl sulfite, mono-ethyl sulfite, mono-butyl sulfite, mono-propyl sulfite, mono-pentyl sulfite, mono-allyl sulfite, mono-benzyl sulfite, dibenzyl sulfite, and mixtures thereof.
 26. The method of claim 24 wherein the additive is present in the electrolyte in a range of about 0.001M to about 0.20M.
 27. The method of claim 24 including discharging the cell to deliver at least one current pulse of an electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse such that the pulse one end potential minus the pulse one minimum potential is less than about 200 mV.
 28. The method of claim 24 including providing the nonaqueous electrolyte comprising a first solvent selected from the group consisting of an ester, an ether, a dialkyl carbonate, and mixtures thereof, and a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester, a cyclic amide, and mixtures thereof.
 29. The method of claim 28 including selecting the first solvent from the group consisting of tetrahydrofuran, methyl acetate, diglyme, triglyme, tetraglyme, 1,2-dimethoxyethane, diisopropylether, 1,2-diethoxyethane, 1-ethoxy,2-methoxyethane, dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethyl methyl carbonate, methyl propyl carbonate, ethyl propyl carbonate, and mixtures thereof.
 30. The method of claim 28 including selecting the second solvent from the group consisting of propylene carbonate, ethylene carbonate, butylene carbonate, acetonitrile, dimethyl sulfoxide, dimethyl formamide, dimethyl acetamide, γ-valerolactone, γ-butyrolactone, N-methyl-pyrrolidinone, and mixtures thereof.
 31. The method of claim 24 including selecting the alkali metal salt from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiO₂, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄, LiCF₃SO₃, and mixtures thereof.
 32. The method of claim 24 including selecting the solid cathode from the group consisting of silver vanadium oxide, copper silver vanadium oxide, vanadium oxide, copper vanadium oxide, and mixtures thereof.
 33. The method of claim 24 including providing the anode comprised of lithium or a lithium-aluminum alloy.
 34. The method of claim 24 including powering an implantable medical device with the electrochemical cell.
 35. A method for reducing voltage delay in a pulse discharging electrochemical cell activated with a nonaqueous electrolyte, comprising the steps of: a) providing an anode comprising an alkali metal; b) providing a cathode including a mixed metal oxide comprised of vanadium oxide and a second metal “SM” selected from the group consisting of Groups IB, IIB, IIIB, IVB, VIB, VIIB and VIII of the Periodic Table of the Elements, the mixed metal oxide having the general formula SM_(x)V₂O_(y) wherein 0.30≦x≦2.0 and 4.5≦y≦6.0; c) activating the electrochemical cell with the nonaqueous electrolyte operatively associated with the anode and the cathode, the nonaqueous electrolyte comprising: i) a first solvent selected from the group consisting of an ester, an ether, a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester, a cyclic amide, and mixtures thereof; iii) an additive of the general formula R¹OS(═O)(OR²) having at least one unsaturated hydrocarbon containing a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon directly connected to the —OSO₂— functional group, wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms; and iv) an alkali metal salt dissolved therein; and d) discharging the cell to deliver at least one current pulse of an electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse such that the pulse one end potential minus the pulse one minimum potential is less than about 200 mV.
 36. A method for reducing voltage delay in a pulse discharging electrochemical cell activated with a nonaqueous electrolyte, comprising the steps of: a) providing an anode comprising an alkali metal; b) providing a cathode including a mixed metal oxide comprised of vanadium oxide and a mixture of copper and a second metal “SM” selected from the group consisting of groups IB, IIB, IIIB, IVB, VIB, VIIB, and VIII of the Periodic Table of the Elements, the mixed metal oxide having the general formula Cu_(x)SM_(y)V₂O_(z) wherein 0.01≦x≦1.0, 0.01≦y≦1.0 and 5.01≦z≦6.5; c) activating the electrochemical cell with the nonaqueous electrolyte operatively associated with the anode and the cathode, the nonaqueous electrolyte comprising: i) a first solvent selected from the group consisting of an ester, an ether, a dialkyl carbonate, and mixtures thereof; ii) a second solvent selected from the group consisting of a cyclic carbonate, a cyclic ester, a cyclic amide, and mixtures thereof; iii) an additive of the general formula R¹OS(═O)(OR²) having at least one unsaturated hydrocarbon directly connected to a C(sp² or sp³)—C(sp³) bond unit having the C(sp³) carbon connected to the —OSO₂— functional group, wherein R¹ and R² are the same or different and they can both be a hydrogen atom or an organic group containing 1 to 12 carbon atoms, and wherein at least R¹ has the structure (R³)(R⁴)(R⁵)C— if R²≠H with at least R³ being an aromatic substituent or an unsaturated organic or inorganic group and wherein if any of the remaining groups of R⁴ and R⁵ is a saturated organic group, the saturated organic group contains 1 to 11 carbon atoms; and iv) an alkali metal salt dissolved therein; and d) discharging the cell to deliver at least one current pulse of an electrical current of a greater amplitude than that of a pre-pulse current immediately prior to the pulse such that the pulse one end potential minus the pulse one minimum potential is less than about 200 mV. 